公司基本資料信息
|
||||||||||||||||||||||||||||
耐寒PC EXL1414T 沙伯基礎SABIC LEXAN PC EXL1414T
LEXAN? EXL1414T resin
聚碳酸酯PC
SABIC Innovative Plastics Asia Pacific
PC EXL1414T 產(chǎn)品說明:
LEXAN EXL1414T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1414T resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications.
物理性能 |
額定值 | 單位制 | 測試方法 |
| 比重 | 1.19 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔體流動速率） (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| 溶化體積流率（MVR） (300°C/1.2 kg) | 9.50 | cm3/10min | ISO 1133 |
| 收縮率 | 內部方法 | ||
| 流動 : 3.20 mm | 0.40 到 0.80 | % | |
| 橫向流動 : 3.20 mm | 0.40 到 0.80 | % | |
| 吸水率 | ISO 62 | ||
| 飽和, 23°C | 0.12 | % | |
| 平衡, 23°C, 50% RH | 0.093 | % | |
| 硬度 | 額定值 | 單位制 | 測試方法 |
| 洛氏硬度 (L 計秤) | 87 | ISO 2039-2 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 拉伸模量 | |||
| -- 3 | 2190 | MPa | ASTM D638 |
| -- | 2310 | MPa | ISO 527-2/1 |
| 抗張強度 | |||
| 屈服 4 | 57.6 | MPa | ASTM D638 |
| 屈服 | 56.8 | MPa | ISO 527-2/50 |
| 斷裂 4 | 59.1 | MPa | ASTM D638 |
| 斷裂 | 55.3 | MPa | ISO 527-2/50 |
| 伸長率 | |||
| 屈服 4 | 5.6 | % | ASTM D638 |
| 屈服 | 5.4 | % | ISO 527-2/50 |
| 斷裂 4 | 120 | % | ASTM D638 |
| 斷裂 | 110 | % | ISO 527-2/50 |
| 彎曲模量 | |||
| 50.0 mm 跨距 5 | 2180 | MPa | ASTM D790 |
| -- 6 | 2120 | MPa | ISO 178 |
| 彎曲應力 | |||
| -- 6, 7 | 88.6 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 5 | 92.0 | MPa | ASTM D790 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
| 簡支梁缺口沖擊強度 8 | ISO 179/1eA | ||
| -30°C | 60 | kJ/m2 | |
| 23°C | 70 | kJ/m2 | |
| 簡支梁無缺口沖擊強度 8 | ISO 179/1eU | ||
| -30°C | 無斷裂 | ||
| 23°C | 無斷裂 | ||
| 懸壁梁缺口沖擊強度 | |||
| -30°C | 710 | J/m | ASTM D256 |
| 23°C | 820 | J/m | ASTM D256 |
| -30°C 9 | 55 | kJ/m2 | ISO 180/1A |
| 23°C 9 | 65 | kJ/m2 | ISO 180/1A |
| 無缺口伊佐德沖擊強度 9 | ISO 180/1U | ||
| -30°C | 無斷裂 | ||
| 23°C | 無斷裂 | ||
| 裝有測量儀表的落鏢沖擊 | ASTM D3763 | ||
| -30°C, Total Energy | 77.4 | J | |
| 23°C, Total Energy | 75.5 | J |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 載荷下熱變形溫度 | |||
| 1.8 MPa, 未退火, 3.20 mm | 121 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 10 | 116 | °C | ISO 75-2/Af |
| 維卡軟化溫度 | |||
| -- | 139 | °C | ASTM D1525 11, ISO 306/B120 11 |
| -- | 138 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | 通過 | IEC 60695-10-2 | |
| 線形熱膨脹系數(shù) | |||
| 流動 : -40 到 95°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| 流動 : 23 到 80°C | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| 橫向 : -40 到 95°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| 橫向 : 23 到 80°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
| 表面電阻率 | > 1.0E+15 | ohms | ASTM D257 |
| 體積電阻率 | > 1.0E+15 | ohms·cm | ASTM D257 |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
| UL 阻燃等級 | UL 94 | ||
| 0.8 mm | HB | ||
| 3.0 mm | V-2 | ||
| 灼熱絲易燃指數(shù) (3.0 mm) | 960 | °C | IEC 60695-2-12 |
| 熱燈絲點火溫度 | IEC 60695-2-13 | ||
| 0.8 mm | 850 | °C | |
| 3.0 mm | 850 | °C |
| 光學性能 | 額定值 | 單位制 | 測試方法 |
| 透射率 (2540 μm) | 82.0 | % | ASTM D1003 |
| 霧度 (2540 μm) | 3.0 | % | ASTM D1003 |
| 注射 | 額定值 | 單位制 | |
| 干燥溫度 | 121 | °C | |
| 干燥時間 | 3.0 到 4.0 | hr | |
| 干燥時間，最大 | 48 | hr | |
| 建議的最大水分含量 | 0.020 | % | |
| 建議注射量 | 40 到 60 | % | |
| 料筒后部溫度 | 271 到 293 | °C | |
| 料筒中部溫度 | 282 到 304 | °C | |
| 料筒前部溫度 | 293 到 316 | °C | |
| 射嘴溫度 | 288 到 310 | °C | |
| 加工（熔體）溫度 | 293 到 316 | °C | |
| 模具溫度 | 71.1 到 93.3 | °C | |
| 背壓 | 0.345 到 0.689 | MPa | |
| 螺桿轉速 | 40 到 70 | rpm | |
| 排氣孔深度 | 0.025 到 0.076 | mm |
耐寒PC EXL1414T 沙伯基礎SABIC LEXAN PC EXL1414T。以上是耐寒PC EXL1414T物性數(shù)據(jù)。如需了解耐寒PC EXL1414T單價、交期或其它塑膠原料信息、請聯(lián)系我們！