沙伯基礎SABIC LEXAN PC EXL1890T 注射成型、食品級。易脫模、高流動、加工性能良好。
LEXAN? EXL1890T resin
聚碳酸酯PC
SABIC Innovative Plastics Asia Pacific
PC EXL1890T 產(chǎn)品說明:
LEXAN EXL1890T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade for food contact applications. This resin offers cold temperature (0 °C) ductility in combination with very high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resin. LEXAN EXL1890T resin offers enhanced release performance and is available in transparent colors and is an excellent candidate for a broad range of applications in food handling or food preparation markets.
| 物理性能 |
額定值 |
單位制 |
測試方法 |
| 比重 |
1.19 |
g/cm3 |
ASTM D792, ISO 1183 |
| 熔流率（熔體流動速率） (300°C/1.2 kg) |
35 |
g/10 min |
ASTM D1238 |
| 溶化體積流率（MVR） (300°C/1.2 kg) |
33.0 |
cm3/10min |
ISO 1133 |
| 收縮率 |
|
|
內(nèi)部方法 |
| 流動 : 3.20 mm |
0.40 到 0.80 |
% |
|
| 橫向流動 : 3.20 mm |
0.40 到 0.80 |
% |
|
| 吸水率 |
|
|
ISO 62 |
| 飽和, 23°C |
0.12 |
% |
|
| 平衡, 23°C, 50% RH |
0.093 |
% |
|
| 硬度 |
額定值 |
單位制 |
測試方法 |
| 洛氏硬度 (L 計秤) |
90 |
|
ASTM D785 |
| 機械性能 |
額定值 |
單位制 |
測試方法 |
| 拉伸模量 |
|
|
|
| -- 2 |
2370 |
MPa |
ASTM D638 |
| -- |
2400 |
MPa |
ISO 527-2/1 |
| 抗張強度 |
|
|
|
| 屈服 3 |
60.0 |
MPa |
ASTM D638 |
| 屈服 |
59.0 |
MPa |
ISO 527-2/50 |
| 斷裂 3 |
58.0 |
MPa |
ASTM D638 |
| 斷裂 |
56.6 |
MPa |
ISO 527-2/50 |
| 伸長率 |
|
|
|
| 屈服 3 |
5.8 |
% |
ASTM D638 |
| 屈服 |
5.4 |
% |
ISO 527-2/50 |
| 斷裂 3 |
120 |
% |
ASTM D638 |
| 斷裂 |
120 |
% |
ISO 527-2/50 |
| 彎曲模量 |
|
|
|
| 50.0 mm 跨距 4 |
2360 |
MPa |
ASTM D790 |
| -- 5 |
2250 |
MPa |
ISO 178 |
| 彎曲應力 |
|
|
|
| -- 5, 6 |
92.9 |
MPa |
ISO 178 |
| 屈服, 50.0 mm 跨距 4 |
99.2 |
MPa |
ASTM D790 |
| 沖擊性能 |
額定值 |
單位制 |
測試方法 |
| 簡支梁缺口沖擊強度 7 |
|
|
ISO 179/1eA |
| -30°C |
40 |
kJ/m2 |
|
| 23°C |
65 |
kJ/m2 |
|
| 簡支梁無缺口沖擊強度 7 |
|
|
ISO 179/1eU |
| -30°C |
無斷裂 |
|
|
| 23°C |
無斷裂 |
|
|
| 懸壁梁缺口沖擊強度 |
|
|
|
| -30°C |
220 |
J/m |
ASTM D256 |
| 23°C |
700 |
J/m |
ASTM D256 |
| -30°C 8 |
30 |
kJ/m2 |
ISO 180/1A |
| 23°C 8 |
60 |
kJ/m2 |
ISO 180/1A |
| 無缺口伊佐德沖擊強度 8 |
|
|
ISO 180/1U |
| -30°C |
無斷裂 |
|
|
| 23°C |
無斷裂 |
|
|
| 裝有測量儀表的落鏢沖擊 (23°C, Total Energy) |
79.0 |
J |
ASTM D3763 |
| 熱性能 |
額定值 |
單位制 |
測試方法 |
| 載荷下熱變形溫度 |
|
|
|
| 1.8 MPa, 未退火, 3.20 mm |
121 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 9 |
118 |
°C |
ISO 75-2/Af |
| 維卡軟化溫度 |
|
|
|
| -- |
138 |
°C |
ASTM D1525 10, ISO 306/B50 10 |
| -- |
140 |
°C |
ISO 306/B120 |
| Ball Pressure Test (125°C) |
通過 |
|
IEC 60695-10-2 |
| 線形熱膨脹系數(shù) |
|
|
|
| 流動 : -40 到 95°C |
6.5E-5 |
cm/cm/°C |
ASTM E831 |
| 流動 : 23 到 80°C |
6.5E-5 |
cm/cm/°C |
ISO 11359-2 |
| 橫向 : -40 到 95°C |
7.4E-5 |
cm/cm/°C |
ASTM E831 |
| 橫向 : 23 到 80°C |
7.4E-5 |
cm/cm/°C |
ISO 11359-2 |
| RTI Elec |
130 |
°C |
UL 746 |
| RTI |
130 |
°C |
UL 746 |
| 電氣性能 |
額定值 |
單位制 |
測試方法 |
| 表面電阻率 |
> 1.0E+15 |
ohms |
ASTM D257 |
| 體積電阻率 |
> 1.0E+15 |
ohms·cm |
ASTM D257 |
| 可燃性 |
額定值 |
單位制 |
測試方法 |
| UL 阻燃等級 (1.5 mm) |
HB |
|
UL 94 |
| 灼熱絲易燃指數(shù) (3.0 mm) |
960 |
°C |
IEC 60695-2-12 |
| 熱燈絲點火溫度 |
|
|
IEC 60695-2-13 |
| 0.8 mm |
825 |
°C |
|
| 3.0 mm |
850 |
°C |
|
| 光學性能 |
額定值 |
單位制 |
測試方法 |
| 透射率 (2540 μm) |
82.0 |
% |
ASTM D1003 |
| 霧度 (2540 μm) |
3.0 |
% |
ASTM D1003 |
| 注射 |
額定值 |
單位制 |
|
| 干燥溫度 |
121 |
°C |
|
| 干燥時間 |
3.0 到 4.0 |
hr |
|
| 干燥時間，最大 |
48 |
hr |
|
| 建議的最大水分含量 |
0.020 |
% |
|
| 建議注射量 |
40 到 60 |
% |
|
| 料筒后部溫度 |
217 到 293 |
°C |
|
| 料筒中部溫度 |
282 到 304 |
°C |
|
| 料筒前部溫度 |
293 到 316 |
°C |
|
| 射嘴溫度 |
288 到 310 |
°C |
|
| 加工（熔體）溫度 |
293 到 316 |
°C |
|
| 模具溫度 |
71.0 到 93.0 |
°C |
|
| 背壓 |
0.345 到 0.689 |
MPa |
|
| 螺桿轉速 |
40 到 70 |
rpm |
|
| 排氣孔深度 |
0.025 到 0.076 |
mm |
|
沙伯基礎SABIC LEXAN PC EXL1890T 注射成型、食品級。易脫模、高流動、加工性能良好。以上是沙伯基礎SABIC LEXAN PC EXL1890T物性數(shù)據(jù)。如需了解沙伯基礎SABIC LEXAN PC EXL1890T單價、交期或其它塑膠原料信息請聯(lián)系我們！